Hydrothermal synthesis of tetragonal BaTiO3 nanotube arrays with high dielectric performance.

Hydrothermal synthesis of tetragonal BaTiO3 nanotube arrays with high dielectric performance.

Journal of nanoscience and nanotechnology (2014-04-18)

Liming Wang, Xiangyun Deng, Jianbao Li, Xinxing Liao, Guoqing Zhang, Chunpeng Wang, Kuifan Su

ABSTRACT

Tetragonal Barium titanate (BaTiO3) nanotube arrays have been prepared using the template-assisted hydrothermal method combined with an annealing process. The in-situ chemical conversion of TiO2 nanotube array templates ensured that BaTiO3 maintained the morphology of the nanotube architectures. Moreover, X-ray diffraction and Raman spectrum characterization were used to confirm that the BaTiO3 nanotube arrays had a tetragonal phase after the use of a simple annealing technique. Typical hysteresis loops showed their ferroelectricity, with the remanent polarization and coercive fields being 2.57 microC/cm2 and 2.52 kV/cm, respectively. The relative dielectric constant of the tetragonal BaTiO3 nanotube arrays reached up to 1000 and the dielectric loss was as low as 0.02 at 1 kHz at room temperature.

MATERIALS

Product Number

Brand

Product Description

GF29584187

Titanium, tube, 500mm, outside diameter 2.03mm, inside diameter 1.55mm, wall thickness 0.24mm, annealed, 99.6+%

GF71783354

Titanium, wire reel, 100m, diameter 0.75mm, as drawn, 99.6+%

GF72193114

Titanium, tube, 500mm, outside diameter 2.03mm, inside diameter 1.63mm, wall thickness 0.2mm, annealed, 99.6+%

GF12869062

Titanium, wire reel, 1m, diameter 0.25mm, as drawn, 99.6+%

GF94150593

Titanium, wire reel, 10m, diameter 1.5mm, as drawn, 99.6+%

GF82635138

Titanium, tube, 500mm, outside diameter 6.35mm, inside diameter 5.53mm, wall thickness 0.41mm, annealed, 99.6+%

GF97204990

Titanium, wire reel, 100m, diameter 0.25mm, annealed, 99.6+%

GF52005596

Titanium, tube, 500mm, outside diameter 9.5mm, inside diameter 8.2mm, wall thickness 0.65mm, annealed, 99.6+%

GF46132534

Titanium, wire reel, 100m, diameter 0.25mm, as drawn, 99.6+%

GF43403431

Titanium, wire reel, 500m, diameter 0.20mm, annealed, 99.6+%

GF40775610

Titanium, wire reel, 1m, diameter 0.20mm, annealed, 99.6+%

GF25479333

Titanium, wire reel, 0.5m, diameter 0.25mm, as drawn, 99.99+%

GF31085760

Titanium, wire reel, 5m, diameter 0.25mm, as drawn, 99.99+%

GF50624434

Titanium, wire reel, 200m, diameter 0.25mm, annealed, 99.6+%

GF55775975

Titanium, wire reel, 25m, diameter 0.25mm, as drawn, 99.6+%

GF75518624

Titanium, wire reel, 20m, diameter 1.5mm, as drawn, 99.6+%

GF08595119

Titanium, wire reel, 100m, diameter 1.0mm, annealed, 99.6+%

GF26602321

Titanium, tube, 500mm, outside diameter 25.4mm, inside diameter 23.62mm, wall thickness 0.89mm, annealed, 99.6+%

GF84917188

Titanium, wire reel, 1m, diameter 0.25mm, as drawn, 99.99+%

GF76266423

Titanium, wire reel, 0.5m, diameter 1.0mm, annealed, 99.6+%

GF90731505

Titanium, tube, 500mm, outside diameter 0.51mm, inside diameter 0.35mm, wall thickness 0.08mm, annealed, 99.6+%

GF95731960

Titanium, tube, 500mm, outside diameter 3.0mm, inside diameter 1.5mm, wall thickness 0.75mm, annealed, 99.6+%

GF71020235

Titanium, wire reel, 0.5m, diameter 1.0mm, as drawn, 99.6+%

GF62738006

Titanium, tube, 500mm, outside diameter 0.81mm, inside diameter 0.61mm, wall thickness 0.1mm, as drawn, 99.6+%

GF06813525

Titanium, wire reel, 1m, diameter 0.5mm, as drawn, 99.6+%

GF16213553

Titanium, wire reel, 10m, diameter 0.125mm, annealed, 99.6+%

GF16602768

Titanium, wire reel, 1m, diameter 0.5mm, as drawn, 99.99+%

GF23860144

Titanium, tube, 500mm, outside diameter 6.35mm, inside diameter 4.57mm, wall thickness 0.89mm, annealed, 99.6+%

GF32919925

Titanium, tube, 500mm, outside diameter 10.3mm, inside diameter 8.7mm, wall thickness 0.8mm, annealed, 99.6+%

GF10374678

Titanium, rod, 500mm, diameter 5mm, annealed, 99.6+%